Since a English, Hatfield has researched austenitic high-manganese steel successfully in 1883, the material had been given "wear resist steel", now is widely used in wear resistant parts in all walks.  
 This steel possesses Austenitic microstructure at room temperature, also known as austenitic high manganese steel. The vast majority of high-manganese steel used for castings. Its microstructure of high-manganese steel guaranteed wear resistance. The chemical composition of the high manganese steel N1, C = 1 2% 4%, Mn = Il% to 14%, P ≤ 0.06%, Si = 0.5% 1 0%, S ≤ O. 03%. High manganese steel castings should be preheated before putting in use. The heated treatment hardness is HB = 179-229. After quenching, the hardness of high-manganese steel is not high, but the strong impact force or pressure will produce hardening phonomenon, the hardness value can be increased to HB = 450 - 550. Hardening is formed just at surface 3-6 mm in depth. This is the reason to high manganese steel's high resistant. High-manganese steel was first used in the production of anti-wear pieces for more than 100 years, which has good strength, toughness, hardening when in use, resistance to abrasive wear, so until now it is still in application. Work principle of BF type
 

Buy on Manufacturer.com

Sell on Manufacturer.com

Community Tools

Company

Click Here to Call Us: 800-928-6710